Large Intercalation Pseudocapacitance in 2D VO2 (B): Breaking through the Kinetic Barrier

"Chuan Xia, Zifeng Lin, Yungang Zhou, Chao Zhao, Hanfeng Liang, Patrick Rozier, Zhiguo Wang, and Husam N. Alshareef" ​Large Intercalation Pseudocapacitance in 2D VO2 (B): Breaking through the Kinetic Barrier
Adv. Mater., DOI: 10.1002/adma.201803594
Chuan Xia, Zifeng Lin, Yungang Zhou, Chao Zhao, Hanfeng Liang, Patrick Rozier, Zhiguo Wang, and Husam N. Alshareef
2D materials; VO2(B); Pseudocapacitance; energy storage
2018
​VO2 (B) features two lithiation/delithiation processes, one of which is kinetically facile and has been commonly observed at 2.5 V versus Li/Li+ in various VO2 (B) structures. In contrast, the other process, which occurs at 2.1 V versus Li/Li+, has only been observed at elevated temperatures due to large interaction energy barrier and extremely sluggish kinetics. Here, it is demonstrated that a rational design of atomically thin, 2D nanostructures of VO2 (B) greatly lowers the interaction energy and Li+‐diffusion barrier. Consequently, the kinetically sluggish step is successfully enabled to proceed at room temperature for the first time ever. The atomically thin 2D VO2 (B) exhibits fast charge storage kinetics and enables fully reversible uptake and removal of Li ions from VO2 (B) lattice without a phase change, resulting in exceptionally high performance. This work presents an effective strategy to speed up intrinsically sluggish processes in non‐van der Waals layered materials.